4 m2/L @ 250 microns
160 ft2/gal @ 10 mils DFT
Polyuretel High-Build UV-Resistant Polyaspartic Floor Coating is a two-component, polyaspartic based, liquid-applied protective floor coating. This fast-curing, very low VOC formulation has a low viscosity with outstanding “wetting” properties, abrasion and UV resistance for colour and gloss stability, with exceptional weathering- and chemical-resistance properties.
- Very low VOCs, fast setting and easy to apply.
- Resistant to weathering and colour fade by ultraviolet rays.
- Wide service temperature range.
- Excellent abrasion and impact resistance.
- Good flow and leveling properties for finishing.
- Excellent gloss retention, hardness and non-yellowing properties.
- High tear resistance and tensile strength.
- Non-staining chemical resistance.
- Adheres to fiberglass, concrete, masonry, plastics, metals and wood.
- May be used to protect walls and other vertical surfaces.
- Available in Slow and Fast Cure versions.
Polyuretel High-Build UV-Resistant Polyaspartic Floor Coating is a roller-, brush- or spray-applied topcoat used in a wide range of institutional, commercial and industrial floor applications where long term durability, impact, abrasion and chemical resistance is required. This product is used as a clear or pigmented protective topcoat used in both interior and exterior applications. Polyuretel is ideal for: Protect epoxy-coated floors against yellowing used in institutional, commercial and industrial areas, Retail stores, office buildings, hotels, casinos, restaurants, entertainment venues, lobbies and other uses where a durable floor surface is required, Food processing plants, pharmaceutical plants and laboratories, Warehouse and production floor areas, as well as Coating metal, aluminum, steel and bronze.
| Colour | Clear and Tinted | |
| Coverage |
(Note: 2 coats recommended for best results) | |
| Mix Ratio |
| |
| Cure Time @ 23°C (75°F) |
| |
| Pot Life - working time @ 23°C (75°F) | 15 minutes | |
| Reducer | Lacquer thinner or IPA | |
| V.O.C. | 30 g/L |
| Method | Results | |
|---|---|---|
| Percent Solids | ASTM D7232-06 | 90% |
| Mixed Viscosity 23°C (75°F) | ASTM D2196 | 1,050 cps |
| Specific Gravity | ASTM D333 |
|
| Tensile Strength | ASTM 695-85 | 6,800 psi |
| Taber Abrasion Resistance | CS-17 wheel | 25 mg, 100 g load, 1000 cycles |
| Elongation | ASTM D638 | 15% |
| Shore D Hardness | 70 | |
| Hardness (7 Days) | ASTM D3363 | 2H |
| Mar Resistance | ASTM D5178 | 1.0 kg |
| QUV Weathering | ASTM D4587 | 90% (1000 hr.-initial) Gloss retention: 80% (final), no chalking |
| Colour Retention | ASTM D4587 | ∆E 1.125 @ 1000 hours |
| Service Temperature Range | -40°C to 120°C |